Decorative Concrete Art Carving by using White Super high strength High belite CSA cement








White Super High Strength High Belite CSA cement grade 82.5

Blaine (Fineness) ≥ 480 m2/kg
Setting time: Initial setting time≥15 mins
Final Setting time: ≤45 mins

Compressive strength: 4 hours ≥ 12.5 Mpa 7 days ≥ 60.0 Mpa 28days ≥82.5Mpa
Flexural Strength: 4 hours ≥ 4.0 Mpa 7 days ≥ 7.0 Mpa 28days ≥8.5 Mpa
Advantages:

1. Fast setting, Rapid hardening, High strength, the real testing value of 4 hours compressive strength could reach 15 Mpa, 102 Mpa in 28 days. Suitable for making the high strength concrete products.

2. Micro Expansion, Low dry shrinkage, the length change is very small. Dry shrinkage rate is just only 1/8-1/10 of portland cement.

3. Have very good anti-corrosion property in sulfate,magnesium salt and seawater. Corrosion resistance coefficient＞1.

4. High impermeability, permeation height is 1/5 of portland cement.

5. High frozen reistance property, can get the strength of critical intensity of cold in 2-3 hours.

6. Low hydration heat release.

7. PH value is under 10.0, Low alkalinity and suitable for GRC products.

8. Whiteness Hunter is above 75.

9. Re-alkali resistant performance is good.

Can be mixed with portland cement in a proper ratio, greatly reduce the shrinkage of portland cement, reduce the cracks.
Applications

GRC/GFRC products, Decoration mortar, Interior and exterior wall putty, Artifical stone and floors, Decorative concrete, Building reinfrocement, HPC and RPC concrete, Rush projects and constructions, projects in winter, High early strength Non shrinkage grouts, etc.

Get more informations by contact: csacement@gmail.com or call: +86 15810326158 (whatsapp), skype: yangjian1886


Comments

Post a Comment

Popular posts from this blog

CSA cement ( CSA binder )

Introduction General characteristics CSA Cement, also named Calcium Sulpho Aluminate Cement with grade: 42.5, 52.5, 62.5, 72.5, 82.5, 92.5, is a hydraulic binder based on calcium sulpho aluminate, rather than calcium aluminates which are the basis of Calcium Aluminates Cement or calcium silicates which are the basis of Portland Cement. It can be used on its own (with a Lithium accelerator), or with an Anhydrite, Portland cement mix, Metakaolin or a combination of all. CSA Cement has the benefit of being readily adaptable to suit many different applications where both rapid set and / or high early strength gain are required. It yields controlled set, enhanced early strengths, shrinkage compensation or expansion and sulphate resistance. Uses include any cement-based product in need of these properties. CSA Cement products exhibit a range of properties to suit a wide spectrum of cement-based applications, like fast setting cements, self-leveling or self-smoothing compounds, sel
Read more

Specialty cement technology-Rapid set CSA cement, High performance of concrete and mortars

Image
CSA cement, full name is Calcium Sulfoaluminate cement, was invented and developed in China since 1970's. It is 100% cement, get ready to use. As the third generation of cements, it is widely used on construction for decades in China. The cement has been used on concrete for bridges, airports, concrete road repair, winter construction and many other applications where early strength and time needed.As well as high strength concrete, high performance of mortars, like Self levelling compounds,tile adhesives,Non shrinkage grouts,etc. The product obtained by grinding cement clinker obtained by roasting suitable raw material, consisting essentially of anhydrous calcium sulphoaluminate and dicalcium silicate. Suitable gypsum and 0-10% limestone shall be blended with clinker during manufacture of rapid-hardening sulphoaluminate cement. The rapid-hardening cement product is hydraulicity binding material. It has high early strength. The code no is R-SAC. Specific surface are
Read more